MJ-IP0943 is a hydrolyzed silane raw material, which can be used in pre-treatment environmental protection conversion coating, with excellent coating performance (salt spray performance and adhesion performance).
It is a silane oligomer, chromium-free pretreatment ，phsphate-free pretreatment.The product can be applied to metal pre-treatment ,metal corrosion pretection and pre-coating treatment.
MJ-IP0945 is a hydrolyzed silane raw material, which can be used in pre-treatment environmental protection conversion coating, with excellent coating performance (salt spray performance and adhesion performance).
It is a silane oligomer, chromium-free pretreatment ，phsphate-free pretreatment.The product can be applied to metal pre-treatment ,metal corrosion pretection and pre-coating treatment.
MJ-IP695 is a modified resin, which can be used in pre-treatment environmental protection conversion coating, with excellent coating performance (salt spray performance and adhesion performance).
It is a silane oligomer, chromium-free pretreatment ，phsphate-free pretreatment.The product can be applied to metal pre-treatment,metal corrosion pretection and pre-coating treatment.
MJ-IP645 is a modified acrylic resin, which can be used in pre-treatment environmental protection conversion coating, with excellent coating performance (salt spray performance and adhesion performance).
It is a silane oligomer, chromium-free pretreatment ，phsphate-free pretreatment.The product can be applied to metal pre-treatment,metal corrosion pretection and pre-coating treatment.
MJ-IP714 is an electron release agent, which can be used in pre-treatment environmental protection conversion coating, with excellent bare film anti-corrosion performance.It is a silane oligomer, chromium-free pretreatment ，phsphate-free pretreatment.The product can be applied to metal pre-treatment ,metal corrosion pretection and green pre-coating treatment.
|
Reference formula (consult Mingjie for details) |
Coating method and substrate |
Coating performance |
|
Fluorozirconic acid+manganese nitrate+MJ-IP0945 |
E-coating (iron, aluminum, zinc, magnesium) |
720-1000h neutral salt spray |
|
Fluorozirconic acid+manganese nitrate+MJ-IP0943 |
E-coating (iron, aluminum, zinc, magnesium) |
500-720h neutral salt spray |
|
Fluorozirconic acid+MJ-IP0943 |
Powder-coating (iron, aluminum, zinc, magnesium) |
720-1000h neutral salt spray |
|
Fluorozirconic acid+MJ-IP0943 |
Paint coating (rolled aluminum) |
2h boiling test, bending test |
|
Fluorozirconic acid+MJ-IP695 |
Powder-coating (aluminum wheel) |
240h Cass; filiform corrosion-general standard |
|
Fluorozirconic acid+MJ-IP645 |
Powder-coating (aluminum profile) |
1000h acid salt spray; 2h high pressure boiling |
|
Fluorozirconic acid+MJ-IP714 |
Die-cast aluminum |
72h bare film anticorrosive neutral salt spray |